Continuous Steel Casting Hole 0.2mm Zirconia Inserts Al2O3-C Body
Zirconia Inserts Introduction
Zirconia inserts are made of zirconia and imported baddeleyite,formed by high tension and baked in high temperature when stablized by special technology.
Different sizes and types of tundish nozzle zirconia inserts are designed and maded according to users' different steel-making conditions and requirements.
Production Process
Our high density of the zirconia nozzle insert with the normal raw material and advanced technology produced is made of the high quality of e-fuzed magnesia and zirconia grain and sand, bonding agent, through the the automatic system mixing, drying, pressing, inspecting, sintering, etc. series system process, then pack into the carton, and wooden box with the desired shipping mark sticked, then deliver to the china mainland and oversea clients.
Inspection times in production process
1. After Mixing, inspect the water content of material,
2. After pressing, inspect the size,missing angle, etc. of semi-finished products
3. After sintering, inspect the size, missing angle, cave, etc. of finished products
4. Before packing, inspect the size, missing angle, cave,of the finished prodcuts again.
Chemical Composition and Physical Propeties
| Model | Chemical Composition | Physical Properties |
| ZrO2 (%) | Al2O3 (%) | SiO2 (%) | MgO (%) | Bulk Density (g/cm3) | Apparent Porosity (%) |
| FMXC-ZN-001 | 95.0 | ---- | ---- | 2.7-3.0 | 5.40-5.45 | 5-7
|
Size Tolerance:
Middle Hole Diamter:+-0.2mm, other sizes: +-1mm.
Exported Countries
India, Pakistan, Iran, Thailand, Turkey, Germany, Peru, USA, etc.
Fangming NewM's Goal
Large size, super special shaped super high temp. zirconia ceramics, we will offer the comprehensive and integrated super high temperature, strong crushing resistance, strong erosion resistance application condition solutions.
Product Tags:
|
|
Hole 0.2mm Zirconia Inserts Al2O3-C Body Continuous Steel Casting Images
|